X-ray CT images of treated soil with different distributions of cementitious solidification materials

figure

posted on 2025-04-10, 07:17 authored by Mai NANAO, Takahito NOZAKI, Yudai FUJIE, Toshifumi MUKUNOKI

Fig.1： 2D vertical cross-sectional image by X-ray CT scanner, (a)Cement-based solidification material added amount is 75kg/m3（Mixing time 10sec）, (b)Cement-based solidification material added amount is 75kg/m3（Mixing time 600sec）, (c)Cement-based solidification material added amount is 120kg/m3（Mixing time 10sec）, (d)Cement-based solidification material added amount is 120kg/m3（Mixing time 600sec）,(e)Cement-based solidification material added amount is 150kg/m3（Mixing time 10sec）, (f)Cement-based solidification material added amount is 150kg/m3（Mixing time 600sec）

Fig.2：3D image after binarization（Threshold：Cement flocculation）, (a)Cement-based solidification material added amount is 75kg/m3（Mixing time 10sec）, (b)Cement-based solidification material added amount is 75kg/m3（Mixing time 600sec）, (c)Cement-based solidification material added amount is 120kg/m3（Mixing time 10sec）,(d)Cement-based solidification material added amount is 120kg/m3（Mixing time 600sec）, (e)Cement-based solidification material added amount is 150kg/m3（Mixing time 10sec）, (f)Cement-based solidification material added amount is 150kg/m3（Mixing time 600sec）

Fig.3：X-ray CT image of treated soil with 75 kg/m3 of cement-based solidification material added, (a)mixing time 10sec（before loading）, (b) mixing time 10sec (strain:0.5％), (c) mixing time 10sec (strain:1.0％), (d) mixing time 10sec (strain:1.5％) , (e) mixing time 600sec (before loading), (f) mixing time 600sec (strain:0.5％)

Fig.4：X-ray CT image of treated soil with 120 kg/m3 of cement-based solidification material added, (a)mixing time 10sec（before loading）, (b) mixing time 10sec (strain:0.5％), (c) mixing time 10sec (strain:1.0％), (d) mixing time 10sec (strain:1.5％) , (e) mixing time 600sec (before loading), (f) mixing time 600sec (strain:0.5％) , (g) mixing time 600sec (strain:1.0％), (h) mixing time 600sec (strain:1.5％)

Fig.5：X-ray CT image of treated soil with 150 kg/m3 of cement-based solidification material added, (a)mixing time 10sec（before loading）, (b) mixing time 10sec (strain:0.5％), (c) mixing time 10sec (strain:1.0％), (d) mixing time 10sec (strain:1.5％) , (e) mixing time 600sec (before loading), (f) mixing time 600sec (strain:0.5％) , (g) mixing time 600sec (strain:1.0％)

History

Corresponding author email address

mai_nanao@taiheiyo-cement.co.jp

Title (in Japanese)

セメント系固化材の分布状況が異なる改良土のX線CT画像

Description (in Japanese)

Fig.1： X線CTより得た2次元鉛直断面画像 (a)セメント系固化材添加量 75kg/m3（撹拌時間 10秒），(b)セメント系固化材添加量75kg/m3（撹拌時間600秒），(c)セメント系固化材添加量 120kg/m3（撹拌時間 10秒），(d)セメント系固化材添加量120kg/m3（撹拌時間600秒），(e)セメント系固化材添加量 150kg/m3（撹拌時間 10秒），(f)セメント系固化材添加量150kg/m3（撹拌時間600秒） Fig.2：二値化処理後の3次元画像(閾値：セメント凝集箇所） (a)セメント系固化材添加量 75kg/m3（撹拌時間 10秒），(b)セメント系固化材添加量75kg/m3（撹拌時間600秒），(c)セメント系固化材添加量 120kg/m3（撹拌時間 10秒），(d)セメント系固化材添加量120kg/m3（撹拌時間600秒），(e)セメント系固化材添加量 150kg/m3（撹拌時間 10秒），(f)セメント系固化材添加量150kg/m3（撹拌時間600秒） Fig.3：載荷時のX線CT画像（セメント系固化材添加量75kg/m3），(a)撹拌時間10秒（載荷前），(b) 撹拌時間10秒 (ひずみ:0.5％)，(c) 撹拌時間10秒 (ひずみ:1.0％), (d) 撹拌時間10秒(ひずみ:1.5％)，(e) 撹拌時間600秒（載荷前），(f) 撹拌時間600秒(ひずみ:0.5％) Fig.4：載荷時のX線CT画像（セメント系固化材添加量120kg/m3），(a)撹拌時間10秒（載荷前），(b) 撹拌時間10秒 (ひずみ:0.5％)，(c) 撹拌時間10秒 (ひずみ:1.0％)，(d) 撹拌時間10秒(ひずみ:1.5％)，(e) 撹拌時間600秒（載荷前），(f) 撹拌時間600秒(ひずみ:0.5％)，(g) 撹拌時間600秒（ひずみ:1.0%），(h) 撹拌時間600秒(ひずみ:1.5％) Fig.5：載荷時のX線CT画像（セメント系固化材添加量150kg/m3），(a)撹拌時間10秒（載荷前），(b) 撹拌時間10秒 (ひずみ:0.5％)，(c) 撹拌時間10秒 (ひずみ:1.0％)，(d) 撹拌時間10秒(ひずみ:1.5％)，(e) 撹拌時間600秒（載荷前），(f) 撹拌時間600秒(ひずみ:0.5％)，(g) 撹拌時間600秒（ひずみ:1.0%）