Effect of Sn Addition on the Anode Properties of SiOx for Lithium-Ion Batteries (Supporting Information)

Download (1.21 MB)
Version 2 2022-05-31, 04:47
Version 1 2022-05-20, 06:07
posted on 2022-05-31, 04:47 authored by Tomoki HIRONO, Hiroyuki USUI, Yasuhiro DOMI, Takahiro NISHIDA, Wataru IRIE, Toshiyuki SAWADA, Hiroki SAKAGUCHI

In this study, we have prepared Sn-added SiOx using a mechanical milling method and investigated the effect of Sn addition on the anode properties of SiOx for lithium-ion batteries.

A charge–discharge cycle test with a charge limit of 1000 mAh g−1 shows that the SiOx electrode causes a capacity fading loss by 170 cycles. Conversely, it is confirmed that the SiOx electrodes with the addition of 1 or 3 wt% of Sn maintain a discharge capacity of up to 250 or 360 cycles, respectively, and the charge–discharge cycle life is extended depending on the amount added. Furthermore, the test is conducted by reducing the lithium-insertion amount from 1000 to 750 mAh g−1 to observe the effect of Sn addition. Resultantly, the difference in cycle life is more pronounced, and the discharge capacity of the 3 wt% Sn-added SiOx is maintained for up to 540 cycles. When the amount of Sn added is as small as 1 wt%, the lithium insertion reaction is locally concentrated because of insufficient electronic conductivity, and Li3.75Si, with a large volume change, is formed. Resultantly, this electrode causes the disintegration of the electrode and a decrease in capacity. However, in the SiOx electrode with 3 wt% of Sn, the reactivity of the lithium ions in the SiO2 matrix is enhanced by the improvement in the electronic conductivity. Thus, the entire active material layer reacts easily and uniformly with the lithium ions. Resultantly, the structure is such that the stress of Si is less likely to concentrate, the damage to the electrodes is reduced, and the electrode disintegration can be suppressed, which is the reason for the enhanced cycle life.


Impurity-doped rutile TiO2 as novel anode materials for next-generation rechargeable battery

Japan Society for the Promotion of Science

Find out more...

In-depth understanding of the silicon lithiation process for next-generation lithium secondary batteries

Japan Society for the Promotion of Science

Find out more...

Creation of next-generation lithium-ion batteries using silicon

Japan Society for the Promotion of Science

Find out more...


Corresponding author email address



© 2022 The Author(s)

Usage metrics





    Ref. manager